Dental Base Metal Alloy
【Product Feature】
This new product spares us from the traditional wax investing and casting , simplifies the PFM procedure greatly and also decrease the possibilities of deformation.What makes our Dental Base Metal Alloy unique is its high precision, good strength,and superior wear-proof performance and better biocompatibility.As the first Dental Base Metal Alloy manufacture of China,XTCERA only produce high quality Dental Base Metal Alloy.
Dental Base Metal Alloy is intended for use in fabrication of porcelain-fused-to metal crown and bridge restorations.
【Technical Data】
Proof strength of 0.2% non-proportional extension >500MPa
Elongation after fracture>2%.
E-module>200GPaDensity:7.9±0.2g/cm3
Vickers hardness:270±27HV10
Corrosion resistance<200μg/cm2
Solidus temperature:1350±50℃,
Liquidus temperature:1410±50℃
Thermal expansion coefficient (CTE) (25 - 500℃):(14.5±0.5)×10 -6/K
Metal-ceramic bond characterization>25MPa
| Cobalt | 66.0wt% |
| Chrome | 28.0wt% |
| Molybdenum | 5.0wt% |
| Silicium | ＜1.0wt% |
| Manganese | ＜1.0wt% |
| Iron | ＜0.8wt% |
| Carbon | ＜0.8wt% |
| Other | ＜2.0wt% |
【Metal-Zironia Junction Surface】【Chemical Composition】
( by Traditional Casting) (Dental Base Metal Alloy)
XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide
Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over
30,000 square meters R&D and production base.
In the past 10 years, XTCERA has sold out about 4000 units dental milling machines and
supplied over 1,000,000 pieces of dental Zirconia blanks per year in the global dental market.
We believe quality is the life of product and trust is the foundation of business relation
Product Tags:
|
|
66.0wt% Cobalt Co-Cr 500MPa Dental Base Metal Alloy Images
|